Tables of Material Data

Table 2: Material Data
Table 2: Material Data
Table 2: Material Data
  • Column 2: The sealing metals indicated are described in table 3.
  • Column 3: a 20-300: Mean linear coefficient of expansion in the temperature range from 20 to 300°C according to DIN 52 328.
  • Column 4: Tg: Transformation temperature according to DIN 52 324
  • Column 5: Viscosity: The indicated viscosity temperatures mark the following processing stages.
    107.6 dPas (softening temperature): Noticeable deformation of glasses under their own weight, even after short heating periods (minutes).
    104 (processing temperature): Central viscosity of the range from 103 to 105 dPas in which most processing techniques such as pressing, blowing and drawing are applied.
  • Column 7: tk100 value: Temperature at which the electrical resistivity is 108 W cm according to DIN 52 326.
  • Column 9: DZ: Dielectric constant; tan d: Dissipation factor.
  • Column 10: W: Resistance to water according to DIN ISO 719
    S: Resistance to acid according to DIN 12 116
    L: Resistance to alkaline solutions according to DIN ISO 695
    W is subdivided into 5 resistance classes, S into 4 and L into 3. The higher the class number, the lower the resistance.
Table 3: Sealing Metals
Table 3: Sealing Metals
Table 3: Sealing Metals
무역박람회 & 이벤트
22.
June
Trade fair Sensors Expo & Conference, San Jose, CA, United States, 22.06 - 24.06.2020
23.
June
Trade fair Sensor+Test, Nuremberg, Deutschland, 23.06 - 25.06.2020
08.
September
Trade fair Gastech, Singapore, 中国, 08.09 - 10.09.2020
09.
September
Trade fair CIOE - China International Optoelectronic Exposition, Shenzhen, 中国, 09.09 - 11.09.2020
연락처
contact-home.png
SCHOTT Korea Co., Ltd.
Seoul 8F. Samseong-Building, 623 Teheran-ro, Gangnam-gu
06173
대한민국
contact-phone.png
E-Mail to SCHOTT+82 2 3456 0328+82 10 2419 7143